Method for processing interior of vapor phase deposition apparatus, method for depositing thin film and method for manufacturing semiconductor device

ABSTRACT

A method for depositing a metal compound film on the wafer by using a vapor phase deposition apparatus  100 , comprising: forming a thin film on the wafer in an interior of the vapor phase deposition apparatus  100  by introducing a source gas for the metal compound film containing Hf or Zr; unloading the wafer having the metal compound film formed thereon from the interior of the vapor phase deposition apparatus  100 ; introducing a reactive gas in the interior of the vapor phase deposition apparatus  100  to immobilize the unreacted organic compound  180  derived from the source gas remained in the interior of the vapor phase deposition apparatus  100 ; loading another wafer in the interior of the vapor phase deposition apparatus  100 ; and depositing metal compound film on another wafer by further introducing the source gas in the interior of the vapor phase deposition apparatus  100 , in the condition that the unreacted organic compound  180  exists therein as an immobilized form, is presented.

This application is based on Japanese patent application NO.2004-164126, the content of which is incorporated hereinto by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a method for processing an interior ofa vapor phase deposition apparatus, a method for depositing a thin filmand a method for manufacturing a semiconductor device.

2. Related Art

In recent years, various innovations on techniques for inhibiting ageneration of particles in a metal compound film are actively made forthe purpose of providing a stable formation of a metal compound filmhaving improved quality by employing a vapor phase deposition apparatus.Typical example of such techniques includes a technique disclosed inJapanese Patent Laid-Open No. 2000-277,459. Japanese Patent Laid-OpenNo. 2000-277,459 describes a technique for nitriding a Ti film disposedon a chamber interior wall or a shower head during a deposition processby containing NH₃ gas and H₂ gas in a deposition gas for depositing ametal compound film including Ti, and further removing chlorine from theformed titanium nitride to provide a film that has better resistance tobe flaked off from the chamber interior wall.

Another typical example of such techniques includes a techniquedisclosed in Japanese Patent Laid-Open No. 2002-134,488. Japanese PatentLaid-Open No. 2002-134,488 describes a technique for fluorinating anSiO₂ film deposited on a chamber interior wall with radical to removethereof, by separately introducing fluorine radical ion in every timeafter the multiple deposition process steps are carried out.

SUMMARY OF THE INVENTION

However, it has now been discovered that the conventional techniquesdisclosed in the above-described literatures still contain a room for animprovement in the following points.

Firstly, the technique described in Japanese Patent Laid-Open No.2000-277,459 involves, in the first place, nitriding the Ti film on thechamber interior wall or on the shower head during the depositionprocess, and thus it is difficult to employ the technique without anymodification to a cleaning process that conducts a cleaning processafter unloading the wafer from the interior of the vapor phasedeposition apparatus.

Further, since the nitriding reaction is a chemical reaction that is notvery reactive, there is a problem of providing lower efficiency for thenitridation of the Ti film on the chamber interior wall or shower head.In addition, since the nitridation is conducted during the depositionprocess, the deposition of the Ti film onto the chamber interior walland the immobilization of the Ti film by the nitridation are notcompatible, and thus it is difficult to provide a sufficient preventionfor the Ti film being flaked off.

Secondly, in the technique described in Japanese Patent Laid-Open No.2002-134,488, concerning an unreacted compound that produces afluorinated compound having relatively lower vapor pressure by afluorinating reaction therewith, such type of unreacted compound ischemically reacted to form a chemical compound having relatively lowervapor pressure even if fluorine radical ion is introduced therein, andtherefore it is difficult to remove such chemical compound by vaporizingthereof.

According to the present invention, there is provided a method forprocessing an interior of a vapor phase deposition apparatus, afterconducting a deposition of a thin film by utilizing an organic sourcematerial within the vapor phase deposition apparatus, comprising:immobilizing an unreacted organic compound within the interior of thevapor phase deposition apparatus, the unreacted organic compound beingderived from the organic source material remained in the interior of thevapor phase deposition apparatus by introducing a reactive gas into theinterior of the vapor phase deposition apparatus.

Since the unreacted organic compound derived from the source gas isimmobilized by the reactive gas according to the present invention,adhesion of the particles of the unreacted organic compound flaked offfrom the chamber interior walls or the like onto the thin film isprevented when the deposition process for the thin film within theinterior of the vapor phase deposition apparatus is conducted, therebyforming the thin film having improved quality stably with higherproduction efficiency.

According to the present invention, there is provided a method forforming a thin film by employing a vapor phase deposition apparatus,comprising: processing an interior of a vapor phase deposition apparatusby employing the method for processing the interior of the vapor phasedeposition apparatus according to the present invention; and forming athin film within the interior of the vapor phase deposition apparatusafter processing the interior of the vapor phase deposition apparatus.

Since the thin film is formed by introducing the source gas into theinterior of the vapor phase deposition apparatus, in which the unreactedorganic compound derived from the source gas has been immobilized by thereactive gas according to the present invention, adhesion of theparticles of the unreacted organic compound flaked off from the chamberinterior walls or the like onto the thin film is prevented, therebyforming the thin film having improved quality stably with higherproduction efficiency.

According to the present invention, there is provided a method formanufacturing a semiconductor device by employing a vapor phasedeposition apparatus, comprising: forming a thin film on a semiconductorsubstrate within an interior of the vapor phase deposition apparatus;unloading the semiconductor substrate having the thin film formed on thesemiconductor substrate from the interior of the vapor phase depositionapparatus after forming the thin film on the semiconductor substrate;processing the interior of the vapor phase deposition apparatus byemploying the method for processing the vapor phase deposition apparatusaccording to the present invention, after unloading the semiconductorsubstrate; and forming a thin film on another semiconductor substrate,after processing the interior of the vapor phase deposition apparatusand loading the another semiconductor substrate in the interior of thevapor phase deposition apparatus.

Since the adhesion of the particles of the unreacted organic compoundflaked off from the chamber interior walls or the like onto the thinfilm is prevented in the interior of the vapor phase depositionapparatus to provide a stable formation of the thin film having improvedquality with higher production efficiency, the semiconductor devicecomprising the thin film having improved quality can be stablymanufactured with higher production efficiency.

While the aspects of present invention have been described as above, itis to be understood that any combination of such aspects is alsoincluded in the scope of the present invention. In addition, anyconversion of the expressions included in the present invention intoanother category is also duly included in the scope of the presentinvention.

For example, while a chemical vapor deposition (CVD) apparatus may bepreferably employed for the vapor phase deposition apparatus describedabove, it is not intended to particularly limit thereto. An atomic layerdeposition (ALD) apparatus or the like may also be employed in stead ofthe CVD apparatus.

It is not necessarily limited to exclusively use the organic sourcematerial described above as the source material for the thin film, andother source materials are also employed in conjunction with the organicsource material. For example, oxidizing source materials and containingoxygen or a chemical compound containing oxygen may be preferablyemployed as other source materials. As such, two types of sourcematerials may be alternately employed to deposit the thin film using aCVD technique or an ALD technique, thereby providing the formation ofthe thin film having improved quality.

In addition, the method for processing the interior of the vapor phasedeposition apparatus may further comprise: removing an immobilizedmaterial from the interior of the vapor phase deposition apparatus afterimmobilizing the unreacted organic compound, the immobilized materialbeing formed by immobilizing the unreacted organic compound.

According to such method, since the immobilized material is removed fromthe interior of the vapor phase deposition apparatus, the adhesion ofthe particles of the unreacted organic compound flaked off from thechamber interior walls or the like onto the thin film is moreeffectively prevented within the interior of the vapor phase depositionapparatus.

In addition, in the method for processing the interior of the vaporphase deposition apparatus, the process for immobilizing the unreactedorganic compound may include introducing an oxidizing gas as thereactive gas.

According to such method, since the unreacted organic compound isoxidized with the oxidizing gas to be effectively immobilized, animproved resistance for the particles derived from the unreacted organiccompound to be flaked off from the chamber interior wall or the like isprovided. As a result, the adhesion of the particles of the unreactedorganic compound flaked off from the chamber interior walls or the likeonto the thin film is prevented.

In addition, in the method for processing the interior of the vaporphase deposition apparatus, the process for immobilizing the unreactedorganic compound may further include additionally introducing anitriding gas as the reactive gas.

According to such method, since the unreacted organic compound isnitrided with the nitriding gas to be effectively immobilized, theeffect of the nitridation synergically acts with the immobilization withthe oxidation, and thus further improved resistance over the particlesderived from the unreacted organic compound being flaked off from thechamber interior wall is provided. As a result, the adhesion of theparticles of the unreacted organic compound flaked off from the chamberinterior walls or the like onto the thin film is further prevented.

In addition, in the method for processing the interior of the vaporphase deposition apparatus, the process for introducing the oxidizinggas may include introducing O₃ gas as the oxidizing gas.

According to such method, since the unreacted organic compound isoxidized with O₃ gas to be more effectively immobilized, due to betteroxidizing property of O₃ gas, a further improved resistance over theparticles derived from the unreacted organic compound being flaked offfrom the chamber interior wall or the like is provided. As a result, theadhesion of the particles of the unreacted organic compound flaked offfrom the chamber interior walls or the like onto the thin film isprevented.

In addition, the organic source material may contain one or moreelement(s) selected from a group consisting of Hf, Zr, La, Pr, Pb, Sr,Ti and Bi.

Even in the case that the deposition of the thin film is conducted inthe vapor phase deposition apparatus by using such organic sourcematerials having lower vapor pressure, the unreacted organic compoundsmay be immobilized by conducting the above-described process afterunloading the wafer. Thus, when another wafer is loaded in the interiorof the vapor phase deposition apparatus thereafter and a deposition of athin film on the another wafer is conducted, the adhesion of theparticles of the unreacted organic compound flaked off from the chamberinterior walls or the like onto the thin film is prevented.

In addition, in the method for manufacturing the semiconductor device,the process for processing the interior of the vapor phase depositionapparatus may be carried out in every time after a plurality ofimplementations of the forming the thin film on the semiconductorsubstrate and the forming the thin film on another semiconductorsubstrate are conducted.

According to such method, since the immobilizing the unreacted organiccompound derived from the source material gas is carried out in everytime after a plurality of implementations of the forming the thin filmon the semiconductor substrate and the forming the thin film on theanother semiconductor substrate are conducted, the process forimmobilizing the unreacted organic compound derived from the source gascan be carried out in the interval between the lot processes for wafersor in every time after the deposition process for a wafer.

Thus, even if the lot processes for the wafers or the depositions forthe wafers are further carried out after immobilizing the unreactedorganic compound derived from the source gas, the adhesion of theparticles of the unreacted organic compound flaked off from the chamberinterior walls or the like onto the thin film is prevented. In addition,since the process for immobilizing the unreacted organic compoundderived from the source gas is all at once conducted in every time aftera plurality of implementations of the formation of the thin film areconducted, the throughput per unit time can be increased. Thus, the thinfilm having higher quality can be stably formed with higher productiveefficiency, according to such process.

In addition, the method for manufacturing the semiconductor device mayfurther comprise removing the immobilized material from the interior ofthe vapor phase deposition apparatus, the immobilized material beingformed by immobilizing the unreacted organic compound.

According to such method, since the immobilized material may be removedfrom the interior of the vapor phase deposition apparatus, the adhesionof the particles of the unreacted organic compound flaked off from thechamber interior walls or the like onto the thin film is moreeffectively prevented within the interior of the vapor phase depositionapparatus.

In addition, in the method for manufacturing the semiconductor device,the process for removing the immobilized material may be carried out inevery time after a plurality of implementations of the immobilizing theunreacted organic compound are carried out.

According to such process, since the immobilized material is all at onceflaked off in every time after a plurality of implementations of theimmobilizing the unreacted organic compound are carried out, thethroughput per unit time can be increased. Thus, the productionefficiency for the thin film is stably improved.

According to the present invention, since the unreacted organic compoundderived from the source gas remained in the interior of the vapor phasedeposition apparatus is immobilized by using the reactive gas, the thinfilm-having higher quality can be stably formed with higher productiveefficiency.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, advantages and features of the presentinvention will be more apparent from the following description taken inconjunction with the accompanying drawings, in which:

FIG. 1 is a schematic cross sectional view of a vapor phase depositionapparatus of an embodiment according to the present invention,illustrating a deposition of a thin film with a first source gas;

FIG. 2 is a schematic cross sectional view of the vapor phase depositionapparatus of the embodiment according to the present invention,illustrating a deposition of a thin film with a second source gas;

FIG. 3 is a schematic cross sectional view of the vapor phase depositionapparatus of the embodiment according to the present invention,illustrating a purging with a purge gas;

FIG. 4 is a schematic cross sectional view of the vapor phase depositionapparatus of the embodiment according to the present invention,illustrating an oxidation of an unreacted compound with O₃ gas;

FIG. 5 is a chart, showing an example of a process sequence formanufacturing a metal compound film by employing the vapor phasedeposition apparatus according to the embodiment;

FIG. 6 is a schematic cross sectional view showing a structure of atransistor according to the embodiment;

FIGS. 7A to 7D are cross sectional process views of the transistor, fordescribing a manufacturing process for the transistor according to theembodiment;

FIGS. 8E and 8F are cross sectional process views of the transistor, fordescribing a manufacturing process for the transistor according to theembodiment; and

FIG. 9 is a cross sectional process views of the transistor, fordescribing a manufacturing process for a capacitor according to theembodiment.

DETAILED DESCRIPTION OF THE INVENTION

The invention will be now described herein with reference toillustrative embodiments. Those skilled in the art will recognize thatmany alternative embodiments can be accomplished using the teachings ofthe present invention and that the invention is not limited to theembodiments illustrated for explanatory purposed.

Embodiments according to the present invention will be described asfollows in further detail, in reference to the annexed figures. In allfigures, identical numeral is assigned to an element commonly appearedin the figures, and the detailed description thereof will not bepresented.

A method for processing an interior of a vapor phase depositionapparatus 100, after conducting a deposition of a thin film (metalcompound film 104) by utilizing an organic source material within thevapor phase deposition apparatus 100, comprises immobilizing anunreacted organic compound 180 within the interior of the vapor phasedeposition apparatus 100, the unreacted organic compound 180 beingderived from the organic source material remained in the interior of thevapor phase deposition apparatus 100 by introducing a reactive gas intothe interior of the vapor phase deposition apparatus 100.

A method for forming a thin film (metal compound film 104) by employinga vapor phase deposition apparatus 100, comprise: processing an interiorof a vapor phase deposition apparatus 100 by employing the method forprocessing the interior of the vapor phase deposition apparatus 100; andforming a thin film within the interior of the vapor phase depositionapparatus 100 after processing the interior of the vapor phasedeposition apparatus 100.

A method for manufacturing a semiconductor device (MOSFET) shown in FIG.6 by employing a vapor phase deposition apparatus 100, comprises:forming a thin film (metal compound film 104) on a semiconductorsubstrate (silicon substrate 400) within an interior of the vapor phasedeposition apparatus 100; unloading the semiconductor substrate havingthe thin film formed on the semiconductor substrate from the interior ofthe vapor phase deposition apparatus 100 after forming the thin film onthe semiconductor substrate; processing the interior of the vapor phasedeposition apparatus 100 by employing the method for processing thevapor phase deposition apparatus 100, after unloading the semiconductorsubstrate; and forming a thin film on another semiconductor substrate,after processing the interior of the vapor phase deposition apparatus100 and loading the another semiconductor substrate in the interior ofthe vapor phase deposition apparatus 100.

First Embodiment

FIG. 1 is a schematic cross sectional view of a vapor phase depositionapparatus 100 of an embodiment according to the present invention,illustrating a deposition of a thin film with a first source gas.

A method for processing an interior of the vapor phase depositionapparatus 100 (cleaning method) according to the present embodiment is amethod for processing an interior of the vapor phase depositionapparatus 100, which is conducted after carrying out a deposition of athin film (after forming a metal compound film on a wafer 104 on asupport 102) by employing an organic source material (a source gasincluding Zr or Hf) transported through a source material container 112and a source material supplying piping 120 into the interior of thevapor phase deposition apparatus (vapor phase deposition apparatus 100),and comprises introducing a reactive gas such as oxidizing gas and thelike in the interior of the vapor phase deposition apparatus 100 throughan oxidizing gas inlet 198 and an oxidizing gas supplying piping 194, toimmobilize the unreacted organic compound derived from the source gas(unreacted organic compound 180) remained in the interior of the vaporphase deposition apparatus 100.

According to this cleaning method (method for providing cleanliness),since the unreacted organic compound 180 derived from the source gasincluding Zr or Hf is immobilized by using the reactive gas such asoxidizing gas and the like, the adhesion of the particles of theunreacted organic compound 180 flaked off from the chamber interiorwalls or the like onto the metal compound film in the wafer 104 mountedon the support 102 is prevented when the metal compound film is formedin the interior of the vapor phase deposition apparatus 100 thereafter.Thus, when the metal compound film is formed by employing the vaporphase deposition apparatus 100, the interior surface of which has beencleaned according to such cleaning method, the metal compound filmhaving higher quality can be stably formed with higher productionefficiency.

In order to more specifically describe the present embodiment, theconfiguration of the vapor phase deposition apparatus 100 shown in FIG.1 will be described as follows.

A supporting member 102 comprising a heater 103 is disposed in theinterior of a chamber 1060. The heater 103 is provided in the support102, and for example, a semiconductor wafer 104 is mounted on thesupport 102, and is heated. A shower head 108 is provided in the upperportion of the chamber 1060, and a gaseous mixture of theabove-described source gas and other types of source gases, an oxidizinggas and a purge gas is sprayed therein through perforations 110 of theshower head 108 according to a predetermined sequence to deposit thethin film on the semiconductor wafer 104.

The vapor phase deposition apparatus 100 comprises four supplyingpipings consisting of a source material supplying piping 120, a sourcematerial supplying piping 130, a purge gas supplying piping 136 and anoxidizing gas supplying piping 194, that are communicated with theshower head 108 of the chamber 1060.

A three way valve 150 and a vaporizer 202 is provided along the sourcematerial supplying piping 120. A piping 116 extended between a three wayvalve 150 and the shower head 108 constitutes one side of the sourcematerial supplying piping 120. A piping 114 extended between thevaporizer 202 and the three way valve 150 constitutes the other side ofthe source material supplying piping 120. In the three way valve 150,one port, which is not connected to the piping 114 or the piping 116, isconnected to a source exhaust piping 210, functioning as a sourceexhaust unit, and a source exhaust slot 212 is provided at a furtherlocation.

In addition, the piping 118 is provided in the opposite side of theshower head 108 opposite to the vaporizer 202 along the source materialsupplying piping 120, and is communicated with the source container 112.The source container 112 is maintained at a room temperature, and iscapable of storing therein a source material such as tetraethyl methylamino zirconium (TEMAZ) and the like in a liquid condition.

A piping 126 in vicinity of the chamber extended between a valve 154 andthe shower head 108 constitutes a portion of the source materialsupplying piping 130. An intermediate region 124 extended between thevalve 154 and the valve 152 also constitutes a portion of the sourcematerial supplying piping 130. A piping 128 remote from the chamberprovided in the opposite side over the valve 152 opposite to the side ofthe shower head 108 also constitutes a portion of the source materialsupplying piping 130, and is communicated with the source materialcontainer 112.

In addition, a purge gas inlet 138 communicates with the shower head 108through the purge gas supplying piping 136 The valve 156 is providedalong the purge gas supplying piping 136, A piping 132 extended betweenthe valve 156 and the shower head 108 constitutes one side of the purgegas supplying piping 136. The piping 134 provided in the opposite sideto the valve 156 opposite to the side of the shower head 108 alsoconstitutes a portion of the purge gas supplying piping 136, and iscommunicated with the purge gas inlet 138.

In addition, the oxidizing gas inlet 198 communicates with the showerhead 108 through the oxidizing gas supplying piping 194. A valve 196 isprovided along the oxidizing gas supplying piping 194. A piping 190extended between the valve 196 and the shower head 108 constitutes aportion of the oxidizing gas supplying piping 194. A piping 192 providedin the opposite side over the valve 196 opposite to the side of theshower head 108 also constitutes a portion of the oxidizing gassupplying piping 194, and is communicated with the oxidizing gas inlet198.

In addition, the lower portion of the chamber 1060 is provided with anoutlet piping 144 and an outlet port 146 communicated with the outletpiping 144 to form a configuration of exhausting the gas that has beenintroduced into the chamber 1060. A valve 158 is provided along theoutlet piping 144 to provide a control for opening and closing of theoutlet piping 144. The outlet piping 144 is branched at the valve 158into a piping 140 and a piping 142.

Next, a process sequence for manufacturing a thin film by using suchvapor phase deposition apparatus will be described.

FIG. 5 is a timing chart, showing an example of a process sequence formanufacturing a metal compound film by employing a vapor phasedeposition apparatus 100 according to the present embodiment. Asdescribed above, a first source gas (“gas A”) is introduced to deposit ametal compound film by using the vapor phase deposition apparatus 100 asshown in FIG. 1, as a first forming process step (step 1). Then, a purgegas (“purge”) is introduced as shown in FIG. 3, as a second formingprocess step (step 2). Subsequently, a second source gas (“gas B”) isintroduced as shown in FIG. 2, as a third forming process step (step 3).Further, a purge gas (“purge”) is introduced as shown in FIG. 3, as afourth forming process step (step 4). These steps are respectivelyconducted in around 0.1 second to 30 seconds.

Repetitions of the deposition via a chemical vapor deposition (CVD)technique or an atomic layer deposition (ALD) technique are conducted byrepeating such sequence to obtain the metal compound film having adesired film thickness. In such case, repetition number of the sequencemay be suitably selected and/or other additional forming processes maybe included, depending upon the purposes.

Then, the sequence is repeated to form the thin film on the wafer, andthereafter, the wafer is unloaded out from the interior of the vaporphase deposition apparatus 100, and then, O₃ gas is introduced as shownin FIG. 4, as a fifth forming process step (step 5).

The sequence is designed to conduct a plurality of implementations ofthe step 1 to the step 4 shown in FIG. 5 in sequence and thereafter thewafer is unloaded and then the step 5 is conducted. More specifically,as shown in FIG. 1 to FIG. 3, the process for supplying the first sourcegas, the process for supplying the purge gas, the process for supplyingthe second source gas and the process for supplying the purge gas aresequentially repeated for multiple times, and then, the wafer having thethin film formed thereon is unloaded from the interior of the vaporphase deposition apparatus 100, and then, the process for supplying theoxidizing gas (reactive gas) such as O₃ gas may be carried out inaccordance with FIG. 4. Then, the unreacted organic compound 180contained in the interior of the vapor phase deposition apparatus 100 isimmobilized by using the oxidizing gas, and thereafter, another wafer isloaded in the vapor phase deposition apparatus 100, and then a pluralityof implementation of the step 1 to the step 4 are conducted in sequenceto form a thin film on another wafer.

As such, after the above-described process sequences are repeated formultiple times, the wafer having the thin film formed thereon isunloaded from the interior of the vapor phase deposition apparatus 100,and then the process for immobilizing the unreacted organic compound 180derived from the source gas with the oxidizing gas such as O₃ gas andthe like is carried out, and thus this means that the process forimmobilizing the unreacted organic compound 180 derived from the sourcegas is conducted between the lot processes for forming the metalcompound film (one lot process can be designed to process 25 pieces ofwafers, for example) or in every time after deposition for the wafer,that is, the process for depositing the film on a wafer.

Having such process, even if the lot processes for the wafers are or thedeposition for the wafer is further carried out after immobilizing theunreacted organic compound 180 derived from the source gas, the adhesionof the particles of the unreacted organic compound 180 flaked off frominterior walls of the chamber 1060 or the like onto the metal compoundfilm can be prevented.

In addition, since the wafer having the thin film formed thereon isunloaded from the interior of the vapor phase deposition apparatus 100and then the process for introducing the oxidizing gas such as O₃ gasfor immobilizing the unreacted organic compound 180 derived from thesource gas is all at once conducted in every time after a plurality ofimplementations of the forming of the thin film are conducted, thethroughput per unit time can be increased. Thus, the metal compound filmhaving higher quality can be stably formed with higher productiveefficiency, according to such process.

Next, status of an operation for depositing a thin film on thesemiconductor wafer employing the vapor phase deposition apparatus 100shown in FIG. 1 will be described. It is noted that FIG. 1 illustrates astatus of opening and shutting the valve, which corresponds to thestatus in the step 1 shown in FIG. 5. The opening/closing statuses ofthe valve are distinguished in the figures by means of providingpatterning, and more specifically, a patterned valve indicates to be inthe closing status, and unpatterned valve indicates to be in the openingstatus.

Since the valve 158 and the three way valve 150 in FIG. 1 are opened,the first source material (for example, TEMAZ) is transferred from thesource material container 112 though the piping 118 and introduced intothe vaporizer 202 in a form of a liquid, and the introduced sourcematerial is heated to be vaporized in the vaporizer 202 in the vaporphase deposition apparatus 100 for depositing the thin film. Further,the vaporized gas is transferred sequentially through the intermediateportion 114, the three way valve 150 and the piping 116, and isintroduced into the chamber 1060 via the perforations 110 of the showerhead 108.

The source gas introduced in the interior of the chamber 1060 reactswith an upper portion of the wafer 104 mounted on the supporting member102. Since the valve 158 is opened, byproducts generated after thereaction and the unreacted source gas are transferred through the piping140, the valve 158 and the piping 142 in this order and are eventuallyexhausted out via the outlet port 146.

Here, since the valve 154 and the valve 152 along the second sourcematerial supplying piping 130 are closed, a second source gas,description of which will be made later, is not supplied. In addition,since the valve 156 along the purge gas supplying piping 136 is alsoclosed, a purge gas, description of which will be made later, is notsupplied. Further, since the valve 196 along the oxidizing gas supplyingpiping 194 is also closed, the reactive gas such as oxidizing gas,description of which will be made later, is not also supplied.

While the available source material in the source material container 112is not particularly limited in the step 1, a source material containinga chemical compound including Hf or Zr, such as HfO₂, ZrO₂ and the like,for example, may be preferably employed for forming the high dielectricconstant film.

Particularly preferable chemical compound including Hf or Zr may be achemical compound containing Hf or Zr, N and a hydrocarbon group, andthe source material containing such compound may be preferably employed.Such chemical compound may be, for example, a compound having a generalformula of: M(NRR′)₄ (where M contains at least one of Hf and Zr, and Rand R′ are same or different hydrocarbon group(s)). R and R′ maypreferably be alkyl group having 6 or less carbons/carbon, and morespecifically, methyl group, ethyl group, propyl group, tertiary butylgroup or the like may be employed. The use of such compounds providesstable deposition of the high dielectric constant film. In addition, theuse of such compounds also inhibits a contamination of particles derivedfrom the organic source material contained in the gaseous sourcematerial, and thus further improvement of the film quality of thedeposited high dielectric constant film can be achieved.

More specifically, the preferable compounds may be: Zr(N(C₂H₅)₂)₄ (tetradiethyl amino zirconium, TDEAZ) or Zr(NCH₃C₂H₅)₄ (TEMAZ) or the like.Selection of such chemical compounds provides a film having a smoothsurface, and prevents a contamination to the film with particles. As aresult, the high dielectric constant film providing lower leakagecurrent and having better film quality can be obtained.

CVD or ALD are conducted via the later-described process utilizing theabove-described source materials, so that a thin film comprisingZrO_(x)C_(y)N_(z) (where x, y and z are selected to satisfy 0<x,0.1≦y≦1.25, 0.01≦z and x+y+z=2) can be obtained. Thin film having suchspecified composition provides higher capacity and considerably reducedleakage current. Therefore, the film can be preferably employed for acapacitor film in a capacitor device, a gate insulating film in a gateelectrode of a transistor and the like.

Here, the deposition temperature for depositing the thin film on theupper portion of the wafer 104 mounted on the support 102 in the case ofemploying Zr(NRR′)₄ as the source material may be preferably 200 degreeC. to 400 degree C., in both occasions of supplying the deposition gasincluding Zr(NRR′)₄ and supplying the oxidizing gas described later.Contamination to the thin film with the impurity can be inhibited byselecting the deposition temperature of not lower than 200 degree C.Further, by selecting the deposition temperature of not higher than 400degree C., particle size of the crystallized particle can be smaller andthe leakage current can be reduced. These temperatures are controlled bythe heater 103 provided within the supporting member 102.

On the other hand, in order to inhibit the deposition onto the chamberwall 106 or the shower head 108, these temperatures are maintained at atemperature that is not higher than the deposition temperature. Morespecifically, the temperature is lower by around 100 degree C. to 200degree C. than the temperature of the wafer 104. When the deposition isconducted by using such temperature condition, the unreacted organiccompound 180 remains on the chamber wall 106 or the shower head 108.

In general, the unreacted organic compound 180 has not been sufficientlyimmobilized on the chamber 1060 or the shower head 108 under suchcondition. Thus, when the quantity of the unreacted organic compound 180is increased, the adhesion of the particles of the unreacted organiccompound 180 flaked off from the interior walls of the chamber 1060 orthe like onto the metal compound film in the wafer 104 mounted on thesupporting member 102 may be occurred. As a result, it is difficult tostably form the metal compound film having higher quality.

On the contrary, the present embodiment involves, after unloading thewafer from the interior of the chamber 1060, introducing the reactivegas such as O₃ gas into the chamber 1060 to immobilize the unreactedorganic compound 180 onto the chamber 1060 or the shower head 108.Therefore, the adhesion of the particles onto the wafer can beinhibited.

FIG. 3 schematically illustrates a status of the vapor phase depositionapparatus 100 according to the present embodiment during theintroduction of the purge gas. This corresponds to the step 2 in FIG. 5.The vapor phase deposition apparatus 100 shown in FIG. 3 hassubstantially the same constitution as the constitution of the vaporphase deposition apparatus 100 shown in FIG. 1, except that the threeway valve 150 along the first source material supplying piping 120communicates with the outlet piping 210 Thus, the supply of the firstsource gas to the chamber is stopped. Further, the valve 152 and thevalve 154 along the second source gas supplying piping 130 are alsoclosed. Thus, the supply of the second source gas is also stopped.

On the other hand, since the valve 156 along the purge gas supplyingpiping 136 is opened, the purge gas in the purge gas inlet 138 istransported through the piping 134, the valve 156 and the piping 132 inthis order, and is introduced into the chamber 1060 from theperforations 110 of the shower head 108. Here, an inert gas representedby N₂, Ar or the like may be employed as the purge gas.

Since the valve 158 is opened, the purge gas introduced into the chamber1060 flushes or purges the residual first source gas remained in thechamber 1060 out, and the flushed residual first source gas istransported sequentially through the piping 140, the valve 158 and thepiping 142 to be exhausted from the outlet port 146.

As such, since the purge gas can be employed to remove most of theunreacted source gas from the interior of the vapor phase depositionapparatus 100, the unreacted organic compound 180 remained in theinterior of the vapor phase deposition apparatus 100 can be reduced.Therefore, in the interior of the vapor phase deposition apparatus 100,the amount of the particles of the unreacted organic compound 180 flakedoff from the interior walls of the chamber 1060 or the like adhered onthe metal compound film on the wafer 104 mounted on the supportingmember 102 can be reduced.

FIG. 2 schematically illustrates a status of the vapor phase depositionapparatus 100 during the introduction of the second source gas. Thiscorresponds to the step 3 in FIG. 5. When the introduction of the purgegas shown in FIG. 3 is completed, then the second source gas isintroduced therein, as shown in FIG. 2. The vapor phase depositionapparatus 100 shown in FIG. 2 has substantially the same constitution asthe constitution of the vapor phase deposition apparatus 100 shown inFIG. 1, except that the three way valve 150 along the first sourcematerial supplying piping 120 communicates with the outlet piping 210.Thus, the supply of the first source gas into the chamber is stopped.Further, the valve 156 along the purge gas supplying piping 136 is alsoclosed. Thus, the supply of the purge gas is also stopped.

On the other hand, since the valve 152 and the valve 154 along thesecond source material supplying piping 130 are opened, the secondsource gas contained in the second source material container 122 istransported sequentially through the piping 128, the valve 152, thepiping 124, the valve 154 and the piping 126, and is introduced into thechamber 1060 from the perforations 110 of the shower head 108.

The second source gas introduced in the interior of the chamber 1060reacts with an upper portion of the wafer 104 mounted on the supportingmember 102. Since the valve 158 is opened, byproducts generated afterthe reaction and the unreacted second source gas are transferred throughthe piping 140, the valve 158 and the piping 142 in this order and areeventually exhausted out via the outlet port 146.

When the thin film having higher dielectric constant is formed byutilizing a source gas containing a chemical compound including Hf or Zras a first source gas, it is preferable to employ an oxidizing gas asthe second source gas. Typical oxidizing gas includes oxygen or achemical compound including oxygen. More specifically, the typicalcompounds may be NO, NO₂, N₂O, H₂O, O₂, O₃ and the like. Among thesecompounds, NO, NO₂ and N₂O are preferable, and gaseous mixture of NO andNO₂ and NO and O₃, which represent combination of nitriding gas andoxidizing gas, are relatively more preferable.

Stable deposition of the high dielectric constant film having betterfilm quality can be obtained by selecting such compounds. Further, whileH₂O is comparatively prone to be remained within the chamber in theprocess employing H₂O that has been frequently employed as an oxidizinggas, NO, N₂O and NO₂ are prone to be removed from the inside of thechamber by purging, thereby improving the productive efficiency.

When the first source gas is metal containing deposition gas and thesecond source gas is an oxidizing gas, it is preferable to select thevolumetric ratio of these compounds (that is, volume of metal containingdeposition gas/volume of oxidizing gas) of equal to or less thancentesimal (1/100). Such volumetric ratio helps reducing impuritiescontained in the film.

When a gaseous mixture of NO and NO₂ is employed as an oxidizing gas,ratio of NO/NO₂ is preferably equal to or less than 1/10000. Thepressure in the deposition process is, for example, within a range offrom 10 mTorr to 10 Torr.

Since the temperature of the chamber wall 106 or the shower head 108 is,in general, lower by around 100 degree C. to 200 degree C. than thetemperature of the wafer 104, the unreacted organic compound 180remained on the portion is not fully oxidized even if the oxidizing gasis employed as the second source gas in this way. Thus, the unreactedorganic compound 180 is not fully immobilized on the chamber wall 106 orshower head 108, and therefore the particles of the unreacted organiccompound 180 may be flaked off from the interior walls of the chamber1060 or the like to be adhered onto the metal compound film in the wafer104 mounted on the supporting member 102 in the interior of the vaporphase deposition apparatus 100.

On the other hand, since the present embodiment involves additionallysupplying the reactive gas such as oxidizing gas under the conditions ofwith sufficiently higher concentration, at sufficiently higher flow rateand for sufficiently longer time than the condition for the caseemploying the oxidizing gas as the second source gas, as shown in FIG. 4described later, the unreacted organic compound 180 remained on theportion can be fully oxidized, even if the temperature of the chamberwall 106 or the shower head 108 is lower by around 100 degree C. to 200degree C. than the temperature of the wafer 104. Thus, the unreactedorganic compound 180 can be fully immobilized on the chamber wall 106 orshower head 108, and therefore the quantity of the particles of theunreacted organic compound 180 flaked off from the interior walls of thechamber 1060 or the like to be adhered onto the metal compound film inthe wafer 104 mounted on the supporting member 102 in the interior ofthe vapor phase deposition apparatus 100 can be reduced.

FIG. 3 schematically illustrates a status of the vapor phase depositionapparatus 100 according to the present embodiment during theintroduction of the purge gas. After completing the introduction of thesecond source gas shown in FIG. 2, then, a purge gas is introducedtherein, as shown in FIG. 3. Here, the process for introducing the purgegas has been described above, and therefore further description thereofwill not be presented here.

FIG. 4 is a schematic cross-sectional view of the vapor phase depositionapparatus 100 according to the present embodiment, illustrating thestructure in oxidizing of an unreacted compound with O₃ gas. As shown inthe above-stated FIG. 1 to FIG. 3, the process for supplying the firstsource gas, the process for supplying the purge gas, the process forsupplying the second source gas and the process for supplying the purgegas are sequentially repeated for multiple times, and then, the waferhaving the thin film formed thereon is unloaded from the interior of thevapor phase deposition apparatus 100, and then, O₃ gas is introduced asshown in FIG. 4.

The vapor phase deposition apparatus 100 shown in FIG. 2 hassubstantially the same constitution as the constitution of the vaporphase deposition apparatus 100 shown in FIG. 1, except that the valve156 along the purge gas supplying piping 136 is closed. Thus, the supplyof the purge gas is stopped.

On the other hand, since the valve 196 along the oxidizing gas supplyingpiping 194 is opened, the reactive gas such as the oxidizing gas withinthe oxidizing gas inlet 198 is sequentially transported through thepiping 192, the valve 196 and the piping 190, and is introduced into thechamber 1060 from the perforations 110 of the shower head 108.

The oxidizing gas introduced in the interior of the chamber 1060chemically reacts with the unreacted organic compound 180 existing onthe surface of the chamber wall 106 or the shower head 108 to form anoxide 182 that is derived by oxidizing the unreacted organic compound180. Since the valve 158 is opened, byproducts generated after thereaction and the unreacted oxidizing gas are transferred through thepiping 140, the valve 158 and the piping 142 in this order and areeventually exhausted out via the outlet port 146.

In this occasion, when the oxidizing gas such as O₃ gas is employed asthe reactive gas, the flow rate of O₃ gas may be selected to be equal toor higher than 100 sccm, for example, and more preferably equal to orhigher than 200 sccm. In addition, the flow rate of O₃ gas may also beselected to be equal to or lower than 2000 sccm, for example, and morepreferably equal to or lower than 1500 sccm. If the flow rate of O₃ gasis within the above-described range, the advantageous effect obtained byoxidizing the unreacted organic compound 180 in the interior of thevapor phase deposition apparatus 100 to immobilize thereof can beimproved.

In addition, the concentration of O₃ gas may be selected to be equal toor higher than 50 g/Nm³, for example, and more preferably equal to orhigher than 100 g/Nm³. Further, the concentration of O₃ gas may beselected to be equal to or lower than 300 g/Nm³, for example, and morepreferably equal to or lower than 250 g/Nm³. If the concentration of O₃gas is within the above-described range, the advantageous effectobtained by oxidizing the unreacted organic compound 180 in the interiorof the vapor phase deposition apparatus 100 to immobilize thereof can beimproved.

In addition, the pressure of O₃ gas may be selected to be equal to orhigher than 0.05 Torr, for example, and more preferably equal to orhigher than 0.1 Torr. Further, the pressure of O₃ gas may be selected tobe equal to or lower than 50 Torr, for example, and more preferablyequal to or lower than 20 Torr. If the pressure of O₃ gas is within theabove-described range, the advantageous effect obtained by oxidizing theunreacted organic compound 180 in the interior of the vapor phasedeposition apparatus 100 to immobilize thereof can be improved.Introduction of O₃ gas into the chamber 1060 may be continued for aduration time, which is longer than that for the oxidation step in theordinary deposition process, for example for not shorter than 30 second,since the unreacted product, which cannot be simultaneously oxidizedduring the deposition step, is oxidized in this step.

Here, the deposition temperature for depositing the metal compound filmin the wafer 104 mounted on the supporting member 102 in the case ofemploying Zr(NRR′)₄ as the source material may be preferably 200 degreeC. to 400 degree C., when the reactive gas such as O₃ gas is supplied.Contamination of the impurity to the metal compound film can beinhibited by selecting the deposition temperature of not lower than 200degree C. Further, by selecting the deposition temperature of not higherthan 400 degree C., particle size of the crystallized particle can besmaller and the leakage current can be reduced. The temperature iscontrolled by the heater 103 provided within the supporting member 102.

Further, temperature of the chamber wall 106 or the shower head 108 maybe preferably 25 degree C. to 150 degree C., when the reactive gas suchas O₃ gas is supplied. Condensation of the source gas on the surface ofthe chamber wall 106 or the shower head 108 can be inhibited byselecting the deposition temperature of not lower than 25 degree C.Formation of the metal compound film on the surface of the chamber wall106 or the shower head 108 can be inhibited by selecting the depositiontemperature of not higher than 150 degree C., and thus the source gascan be effectively utilized.

Advantageous effects obtained by the present embodiment will bedescribed as follows.

According to the present embodiment, a source gas containing Hf or Zr isfurther introduced under the condition of having the immobilizedunreacted organic compound 180 in the interior of the vapor phasedeposition apparatus 100. Thus, even if the metal compound film isfurther formed due to the source gas, the adhesion of the particles ofthe unreacted organic compound 180 flaked off from the interior walls ofthe chamber 1060 or the like onto the metal compound film in the wafer104 mounted on the supporting member 102 is prevented, and thus themetal compound film having higher quality can be stably formed withhigher productive efficiency.

In addition, according to the present embodiment, since the wafer havingthe thin film formed thereon is unloaded from the interior of the vaporphase deposition apparatus 100 and then the process for immobilizing theunreacted organic compound 180 derived from the source gas is conductedin every time after a plurality of implementations of process forintroducing the source gas containing Hf or Zr, the process forimmobilizing the unreacted organic compound 180 derived from the sourcegas can be carried out in every time in the interval between the lotprocesses for the metal compound films or in every time after thedeposition process for a wafer.

Thus, even if another wafer having no thin film formed thereon is loadedin the interior of the vapor phase deposition apparatus 100 and the lotprocesses for the wafers or the depositions for the wafers are furthercarried out after immobilizing the unreacted organic compound 180derived from the source gas, the adhesion of the particles of theunreacted organic compound 180 flaked off from interior walls of thechamber 1060 or the like onto the metal compound film in the wafer 104mounted on the supporting member 102 is prevented.

Further, since the wafer having the thin film formed thereon is unloadedfrom the interior of the vapor phase deposition apparatus 100 and thenthe process for immobilizing the unreacted organic compound derived fromthe source gas is all at once conducted, after the processes for formingthe thin film on one piece of wafer are conducted for a plurality ofwafer, the throughput per unit time can be increased. Thus, the metalcompound film having higher quality can be stably formed with higherproductive efficiency, according to such process.

More specifically, in the vapor phase deposition apparatus 100 fordepositing an oxide containing compound containing Zr or Hf by employinga deposition source material having lower vapor pressure such as asource gas containing Zr(NRR′)₄ or Hf(NRR′)₄ according to the presentembodiment, the unreacted organic compound 180 containing Zr(NRR′)₄ orHf(NRR′)₄, which is remained in the interior of the chamber 1060, isimmobilized by conducting the oxidation process with the oxidizing gassuch as O₃ gas after unloading the wafer having the thin film formedthereon from the interior of the vapor phase deposition apparatus 100and before conducting the next deposition process, so that when anotherwafer is loaded in the interior of the vapor phase deposition apparatus100 thereafter and a deposition of a thin film is conducted, theadhesion of the particles flaked off from the interior walls of thechamber 1060 or the like onto the wafer 104 is prevented.

Since the source gas containing Zr(NRR′)₄ or Hf(NRR′)₄, which asrelatively lower vapor pressure, is prone to be remained within thechamber 1060 as the unreacted organic compound 180, it is difficult toremove thereof using an ordinary gas cleaning process or a purgeprocess. Further, a non-reactive gas or an inert gas is employed in thepurge process for the interior of the chamber 1060 when the vapor phasedeposition apparatus 100 is not employed in the conventional technology,and therefore it is difficult to reduce the generation of the particles.

When the deposition is conducted under such condition, particles may begenerated on the wafer 104 during the introduction of theabove-described second source gas having higher oxidizing property, dueto an accumulation of the unreacted organic compound 180 in the interiorof the chamber 1060. It is considered that the possible cause may bethat the unreacted organic compound 180 remains in portions of lowertemperature in the interior of the chamber 1060, and a contact angle ofthe particles of the unreacted organic compound 180 with the chamberwall 106 exceeds a critical angle during the deposition process and theparticles are flaked off from the chamber wall 106 and adheres on thewafer. Here, the phenomenon of generating the particles on the wafer 104due to the residual unreacted organic compound 180 in the interior ofthe chamber 1060 is discovered by the present inventors for the firsttime, and the cause thereof has not been found in the conventionaltechnique.

In the present embodiment, the unreacted organic compound 180 containingZr(NRR′)₄ or Hf(NRR′)₄ remained in the interior of the chamber 1060 isimmobilized by oxidizing thereof with an oxidizing gas having higheroxidizing property in the process for processing the interior of thechamber 1060 before depositing the metal compound film on the wafer 104.Thus, the generation of the particles on the wafer 104 can be inhibitedwhen the wafer 104 is loaded into the interior of the chamber 1060 toconduct the process for depositing the thin film thereon.

On the other hand, in the technique described in Japanese PatentLaid-Open No. 2000-277,459, particles consisting of inorganic compoundsare generated and these compounds are nitrided so as to inhibit theflaking off from the chamber interior wall or the shower head. However,the nitridation process is conducted simultaneously with conducting thedeposition process in the first place in the technology of JapanesePatent Laid-Open No. 2000-277,459, and thus the technique is hardlyapplicable to the cleaning process that conducts after unloading thewafer from the vapor phase deposition apparatus without anymodification.

On the contrary, in the technique of the present embodiment, a pluralityof the deposition processes are repeated by using the organic sourcematerial of larger molecular weight containing an element of largeatomic number such as Hf or Zr, and then, the wafer having the thin filmformed thereon is unloaded from the vapor phase deposition apparatus100, and thereafter, the reactive gas is additionally introduced. Then,the organic source material having lower vapor pressure due to the itslarger molecular weight as described above and polymers thereof,remained in the interior of the vapor phase deposition apparatus 100 ina liquid form, are immobilized by decarbonizing from molecules of theunreacted organic compound 180. As such, the technique according to thepresent embodiment is definitely different from the technique describedin the Japanese Patent Laid-Open No. 2000-277,459.

Further, the present embodiment involves, after a plurality of thedeposition processes are repeated and the wafer is unloaded from theinterior of the vapor phase deposition apparatus 100, immobilizingprocess for oxidizing the unreacted organic compound 180 to immobilizethereof is carried out, and therefore the throughput per unit time canbe improved. Further, after the processed wafer having the thin filmdeposited thereon is unloaded from the interior of the vapor phasedeposition apparatus 100, another wafer having no thin film formedthereon is loaded in the interior of the vapor phase depositionapparatus 100 and the thin film is formed thereon, and thereafter, theimmobilizing process for oxidizing the unreacted organic compound 180 toimmobilize thereof may be carried out. This operation improves thethroughput per unit time. In other words, the immobilizing process forimmobilizing the unreacted organic compound 180 may be carried out, inevery time after a plurality of implementations of the forming the thinfilm on the wafer and the forming the thin film on another wafer areconducted.

On the other hand, Japanese Patent Laid-Open No. 2002-134,488 describesa technique for fluorinating a SiO₂ film deposited on a chamber interiorwall with radicals to remove thereof, by additionally introducingfluorine radical ion after the deposition process steps are repeated formultiple times. When a fluorination is conducted by utilizing radicals,compounds, which are not fluorinated by the thermal fluorination, aresuccessfully fluorinated, and thus can be removed from the chamber.

On the contrary, the present embodiment employs the organic sourcematerial containing a heavy metal such as Hf or Zr. Therefore, even ifthe unreacted organic compound 180 derived from the organic sourcematerial is fluorinated by radicals, the vapor pressure of the obtainedfluoride is lower, as shown in Table 1, and thus it is difficult toconduct the gas cleaning process in the case of employing the techniquedescribed in Japanese Patent Laid-Open No. 2002-134,488. Here, thepresent embodiment employs a method for immobilizing the unreactedorganic compound 180 with the reactive gas such as oxidation gas. Assuch, the technique according to the present embodiment is definitelydifferent from the technique described in the Japanese Patent Laid-OpenNo. 2002-134,488. TABLE 1 VAPOR PRESSURE AT 100 DEGREE C. Material TiF₄ZrF₄ TiCl₄ HfCl₄ ZrCl₄ Vapor 4 × 10⁻² 3 × 10⁻²² 3 × 10² 6 × 10⁻³ 2 ×10⁻³ pressure (Torr)

The reason for employing the method for immobilizing the unreactedorganic compound 180 by oxidizing thereof with O₃ gas in the presentembodiment according to the present invention, instead of employing thegas cleaning process of the interior of the chamber 1060 of the vaporphase deposition apparatus 100 by using fluorine gas or chlorine gas,will be described as follows.

When the cleaning of the interior of the vapor phase depositionapparatus 100 is conducted, chlorine containing gas or fluorinecontaining is often employed. For example, residual materials containingTi, TiN or the like is capable of being removed by the gas cleaningprocess with ClF_(x). However, when Zr or Hf is employed, chlorinecontaining or fluorine containing compounds with Zr or Hf have lowervapor pressure by five digits or more than the case of employing Ti.Therefore, the unreacted organic compound 180 containing Zr or Hf isdifficult to be gas-cleaned with fluorine gas or chlorine gas. In thisreason, in the present embodiment, the method for immobilizing theunreacted organic compound 180 by oxidizing thereof is employed.

In the present embodiment, the unreacted organic compound 180 (deposit)adhered onto the chamber wall 106 of the vapor phase depositionapparatus 100 is removed mechanically after the unreacted organiccompound 180 is immobilized. Alternatively, a detachable liner is usedfor protecting the chamber wall 106, and the unreacted organic compound180 can be removed by replacing the liner. The mechanical cleaning maybe done, after the immobilized film thickness on the chamber wall 106become the predetermined one by forming the thin film on a plurality ofsemiconductor substrate and immobilizing the film on the chamber wall106.

Here, in the case that the removal thereof is conducted by mechanicalremoval or liner replacement removal in such way, an additionalmanufacturing process step is not particularly required, even ifunreacted organic compound 180 adhered onto the chamber wall 106 isfurther oxidized to be immobilized (coagulated), and therefore theproduction efficiency thereof is not particularly deteriorated.

The reason that it is more preferable to employ the method forimmobilizing the unreacted organic compound 180 in the interior of thechamber 1060 of the vapor phase deposition apparatus 100 by oxidizingthereof with O₃ gas in the present embodiment according to the presentinvention, rather than nitriding thereof with ammonia gas or the like,will be more specifically described.

The unreacted organic compound 180 is a substance consisting of acomposition contain relatively larger amount of carbon, and may berepresented by a chemical formula of, for example,ZrO_(x)C_(y)N_(z)H_(w). In this occasion, carbon contained in moleculeof the unreacted organic compound 180 is decarbonized in a form of CO₂or the like together with H₂O by introducing O₃, As such, carbon inmolecule of the unreacted organic compound 180 is decarbonized toprovide a solid film containing smaller amount of carbon, therefore theunreacted organic compound 180 is further immobilized onto the chamberwall 106.

Further, as shown in the following Table 2, concerning the chemicalcompound containing Zr or Hf, the oxidizing reaction of such compoundgenerally presents more formation energy than the nitriding reaction ofsuch compound, and thus the reactivity of the oxidizing reaction thereofis higher than the nitriding reaction thereof, and therefore theefficiency for immobilizing the unreacted organic compound 180 isimproved by oxidizing thereof with O₃ gas to immobilize thereof. TABLE 2FORMATION ENERGY AT 25 DEGREE C. (kcal/mol) O (Oxidation) N(Nitridation) Zr −263.1 −88.0 Hf −266.0 −88.2

Thus, the chemical compound containing Zr or Hf is prone to form anoxide thereof rather than a nitride thereof, and it is preferable in thepresent embodiment to employ the method for oxidizing the interior ofthe chamber 1060, so that the unreacted organic compound 180 is moreeffectively immobilized.

In addition, when the metal compound film is formed by using vapor phasedeposition apparatus 100, the first source gas containing Zr or Hf isemployed together with the second source gas containing O₃ gas or thelike as the source gas for the deposition, as described above. Thus, O₃gas as the second source gas is used as the reactive gas forimmobilizing the unreacted organic compound 180, so that the apparatusconfiguration of the vapor phase deposition apparatus 100 can besimplified, thereby reducing the manufacturing cost for the vapor phasedeposition apparatus 100.

Second Embodiment

In the present embodiment, a proper amount of a nitriding gas such asammonia or nitrogen is employed in addition to the oxidizing gas such asO₃ gas as the reactive gas for immobilizing the unreacted organiccompound 180 during the oxidation process, to immobilize the unreactedorganic compound 180 containing ZrO_(x)C_(y)N_(z)H_(w) by decarbonizingfrom molecule of the unreacted organic compound 180. Here, a point thatis not particularly described in the present embodiment is similar to apoint described in the first embodiment. The vapor phase depositionapparatus 100 described in the first embodiment shown in FIG. 1 may beemployed for the vapor phase deposition apparatus of the presentembodiment.

As such, the nitriding gas such as NH₃ may be employed in addition tothe oxidizing gas such as O₃ gas to oxynitriding the unreacted organiccompound 180, thereby effectively immobilizing the unreacted organiccompound.

In this occasion, when the oxidizing gas such as O₃ gas is employed asthe reactive gas, the flow rate of O₃ gas may be selected to be equal toor higher than 100 sccm, for example, and more preferably equal to orhigher than 200 sccm. In addition, the flow rate of O₃ gas may also beselected to be equal to or lower than 2000 sccm, for example, and morepreferably equal to or lower than 1500 sccm. If the flow rate of O₃ gasis within the above-described range, the advantageous effect obtained byoxynitriding the unreacted organic compound 180 in the interior of thevapor phase deposition apparatus 100 to immobilize thereof can beimproved.

In addition, the concentration of O₃ gas may be selected to be equal toor higher than 50 g/Nm³, for example, and more preferably equal to orhigher than 100 g/Nm³. Further, the concentration of O₃ gas may beselected to be equal to or lower than 300 g/Nm³, for example, and morepreferably equal to or lower than 250 g/Nm³. If the concentration of O₃gas is within the above-described range, the advantageous effectobtained by oxynitriding the unreacted organic compound 180 in theinterior of the vapor phase deposition apparatus 100 to immobilizethereof can be improved.

In addition, the pressure of O₃ gas may be selected to be equal to orhigher than 0.05 Torr, for example, and more preferably equal to orhigher than 0.1 Torr. Further, the pressure of O₃ gas may be selected tobe equal to or lower than 50 Torr, for example, and more preferablyequal to or lower than 20 Torr. If the pressure of O₃ gas is within theabove-described range, the advantageous effect obtained by oxynitridingthe unreacted organic compound 180 in the interior of the vapor phasedeposition apparatus 100 to immobilize thereof can be improved.

In such case, when NH₃ gas is employed in addition to the oxidizing gassuch as O₃ gas, the flow rate of NH₃ gas may be selected to be equal toor higher than 1 sccm, for example. In addition, the flow rate of NH₃gas may also be selected to be equal to or lower than 2000 sccm, forexample. If the flow rate of NH₃ gas is within the above-describedrange, the advantageous effect obtained by oxynitriding the unreactedorganic compound 180 in the interior of the vapor phase depositionapparatus 100 to immobilize thereof can be improved. Here,concentration, pressure or the like of NH₃ gas may be appropriatelyselected to provide a preferable range, according to process conditions.

Here, the nitriding gas described above is not limited to NH₃ gas, andother gas such as, for example, N₂ gas, may also be employed. Inaddition, a timing for introducing the nitriding gas such as NH₃ gasinto the chamber 1060 may be the same time as the timing for introducingthe oxidizing gas such as O₃ gas, or may be either after or beforethereof.

The technique in Japanese Patent Laid-Open No. 2000-277,459 describesthat the nitridation of the unreacted compound in the interior of thechamber 1060 is carried out by utilizing a gaseous mixture of NH₃ andH₂.

On the contrary, the nitriding gas such as NH₃ is employed in additionto the oxidizing gas such as O₃ gas in the above-described embodiment,so that the unreacted organic compound 180 is oxynitrided to beimmobilized, and therefore the unreacted organic compound 180 can beimmobilized more effectively than the case of introducing NH₃ gas alone.As such, the technique according to the present embodiment is alsodefinitely different from the technique described in the Japanese PatentLaid-Open No. 2000-277,459.

Here, when NH₃ gas is flowed in addition to the oxidizing gas such as O₃gas, an inert gas such as Ar may also be simultaneously flowed togetherwith NH₃ gas.

In addition, the deposition temperature for depositing the metalcompound film in the wafer 104 mounted on the supporting member 102 inthe case of employing Zr(NRR′)₄ as the source material may be preferably200 degree C. to 400 degree C., when the nitriding gas such as a gascontaining NH₃ is supplied in addition to the oxidizing gas such as O₃gas. Contamination of the impurity to the metal compound film can beinhibited by selecting the deposition temperature of not lower than 200degree C. Further, by selecting the deposition temperature of not higherthan 400 degree C., particle size of the crystallized particle can besmaller and the leakage current can be reduced. The temperature iscontrolled by the heater 103 provided within the supporting member 102.

Further, temperature of the chamber wall 106 or the shower head 108 maybe preferably 25 degree C. to 150 degree C., when the nitriding gas suchas a gas containing NH₃ is supplied in addition to the oxidizing gassuch as O₃ gas. Condensation of the source gas on the surface of thechamber wall 106 or the shower head 108 can be inhibited by selectingthe deposition temperature of not lower than 25 degree C. Formation ofthe metal compound film on the surface of the chamber wall 106 or theshower head 108 can be inhibited by selecting the deposition temperatureof not higher than 150 degree C., and thus the source gas can beeffectively utilized.

In addition, when the nitriding gas such as a gas containing NH₃ issupplied in addition to the oxidizing gas such as O₃ gas, a remoteplasma may be utilized to oxynitride the unreacted organic compound 180,thereby immobilizing the unreacted organic compound.

Third Embodiment

The present embodiment relates to a method for forming a thin film byusing an organic source material containing a heavy metal except Hf orZr. The method for depositing a thin film according to the presentembodiment is the substantially same as the method described in thefirst embodiment or the second embodiment except the following points.

While in the above-described embodiment, various types of amino acidscontaining TEMAZ or the like as a source gas is employed, other sourcegas having lower vapor pressure may also be employed. Also in such case,since the unreacted compound of a source gas can be immobilizedaccording to the method for depositing the metal compound film of thepresent invention, the high dielectric constant film having higherquality can similarly be obtained with higher stability.

More specifically, organic source materials containing a heavy metalsuch as La, Pr, Pb, Sr, Ba, Cu, Ti, Bi and the like and having a vaporpressure of equal to or lower than 1 Torr at 100 degree C. can beemployed as an organic source material in the present embodiment.Further, an alternative organic source material may be a compound, whichis constituted of a heavy metal such as Hf, Zr, La, Pr, Pb, Sr, Ba, Cu,Ti, Bi and the like and an organic ligand having larger molecular weightcoordinated around the heavy metal, such as N(C₂H₅CH₃), N((C₂H₅)₂),OtBu, OiPr, 1-(2-methoxy ethoxy)-2,2,6,6-tetra methyl-3,5-heptanedionate (METHD), 6-methyl-2,4-heptane dionate (MHD),1-methoxy-2-methyl-3-propoxide (MMP) and the like.

TEMAZ (Zr(NC₂H₅CH₃)₄) employed in the first embodiment and the secondembodiment has a vapor pressure of 0.5 Torr at 90 degree C., and TEMAH(Hf(NC₂H₅CH₃)₄) has a vapor pressure of 1 Torr at 87 degree C. On theother hand, TiN formed by using an inorganic source material can becleaned by utilizing a chlorine containing gas, and the chloridethereof, that is, TiCl₄, has a vapor pressure of 3×10² Torr at 100degree C.

In the case of employing such organic source material having lower vaporpressure, the unreacted organic compound 180 having lower vapor pressurecan be oxidized by using the oxidizing gas using a method similar to themethod for depositing the thin film described in the first embodiment toeffectively immobilize the unreacted organic compound. Alternatively,the unreacted organic compound 180 can also be oxynitrized by using agaseous mixture of the oxidizing gas and the nitriding gas using amethod similar to the method for depositing the thin film described inthe second embodiment to effectively immobilize the unreacted organiccompound.

Therefore, the generation of the particles on the wafer 104 can beinhibited even if the wafer 104 is loaded in the interior of the chamber1060 and the deposition process of the thin film is conducted. As aresult, the semiconductor device having better reliability can be stablymanufactured with higher production efficiency.

Fourth Embodiment

The present embodiment illustrates an example of applying the presentinvention to a metal oxide semiconductor field effect transistor(MOSFET). MOSFET according to the present embodiment has a structureshown in FIG. 6. The MOSFET (transistor) shown in FIG. 6 comprises, on asilicon substrate 400, a gate electrode, which includes a multilayeredbody of a gate insulating film composed of a multi-layered body of asilicon oxynitride film 402 and a metal compound film 404, and a gateelectrode 406 composed of polysilicon. Side walls 410 composed of asilicon oxide film are formed on side faces of the gate electrode. Asource region and a drain region 412 containing an impurity diffusedtherein are formed on the face of the silicon substrate 400 in bothsides of the gate electrode.

The metal compound film 404 has a chemical composition represented byHfO_(x)C_(y)N_(z) (where x, y and z are selected to satisfy 0<x,0.1≦y≦1.25, 0.01≦z and x+y+z=2). Penetration of an impurity in the gateelectrode into the silicon substrate can be effectively inhibited byemploying such film.

Preferable source gas for depositing the metal compound deposition mayinclude Hf(N(C₂H₅)₂)₄, Hf(N(CH₃)₂)₄, Hf(N(CH₃)(C₂H₅))₄, Zr(N(C₂H₅)₂)₄,Zr(N(CH₃)₂)₄, Zr(N(CH₃)(C₂H₅))₄ and the like. Penetration of an impuritycan be more effectively inhibited by employing such compound.

A manufacturing process for the MOSFET shown in FIG. 6 will be describedin reference with FIGS. 7A to 7D and FIGS. 8E and 8F. Firstly, as shownin FIG. 7A, a silicon substrate 400 that has been cleaned its surface byusing a predetermined liquid chemical solution is prepared. Then, asshown in FIG. 7B, a silicon oxynitride film 402 is formed on a mainsurface of the silicon substrate 400 using a chemical vapor deposition(CVD) technique. Subsequently, as shown in FIG. 7C, a metal compoundfilm 404 is formed using an atomic layer deposition (ALD) technique.Among the deposition gases employing in this deposition process, a metalcompound represented by a general formula of Hf(NRR′)₄ can be employedfor a metal source gas (where R and R′ are same or different hydrocarbongroup(s), and preferably linear or branched alkyl group). R and R′ maypreferably be alkyl group having 6 or less carbons/carbon, and morespecifically, methyl group, ethyl group, propyl group, tertiary butylgroup or the like may be employed.

On the other hand, typical oxidizing gas employed for depositing themetal compound film 404 includes oxygen or a chemical compoundcontaining oxygen. More specifically, the typical compounds may be NO,NO₂, N₂O, H₂O, O₂, O₃ and the like. Among these compounds, NO, NO₂ andN₂O are preferable, and a gaseous mixture of NO and NO₂ and a gaseousmixture of NO and O₃, which represent combinations of nitriding gas andoxidizing gas, are more preferable. Stable deposition of the capacitorfilm having better film quality can be obtained by selecting suchcompounds. Further, NO, N₂O and NO₂ are easier to be removed from thedeposition apparatus by purging, thereby improving the productiveefficiency.

Here, in the deposition process for the metal compound film 404, any oneof the methods for depositing the metal compound film described in thefirst embodiment or the second embodiment is employed.

The supply of the deposition gas is conducted as follows, for example.Firstly, Hf(N(CH₃)(C₂H₅))₄ is supplied as a source material in aninterior of a chamber 1060 of an ALD apparatus to cause a chemicalreaction on a surface of a lower electrode thin film, so that one atomiclayer is deposited thereon. Next, the supply of Hf(N(CH₃)(C₂H₅))₄ isstopped, and then, an inert gas, typical example of which include N₂, Aror the like, is introduced into the chamber 1060 as a purge gas to purgeor flush the excess amount of unreacted Hf(N(CH₃)(C₂H₅))₄ out.

Next, NO gas is supplied therein to remove functional group thatterminates Hr deposited on the substrate. Subsequently, the supply of NOgas is stopped, and an inert gas, typical example of which include N₂,Ar or the like, is introduced therein as a purge gas to purge or flushunreacted NO and/or byproducts generated after reaction, and then thesupply of the purge gas is stopped.

As described above, a desired number of the sequential process cycleconsisting of the supply of Hf(N(CH₃)(C₂H₅))₄, the first purge, thesupply of NO and the second purge are repeated to obtain the thin metalcompound 404 consisting of HfO_(x)C_(y)N_(z) having a film thickness of5 to 15 nm (where x, y and z are selected to satisfy 0<x, 0.1≦y≦1.25,0.01≦z and X+y+z=2).

Thereafter, a gate electrode film 406 is formed on the metal compoundfilm 404, as shown in FIG. 7D. It is preferable to employpolycrystalline silicon for the gate electrode film 406, and otherwise,a metal electrode such as SiGe, TiN, WN, Ni and the like can also beemployed.

Subsequently, as shown in FIG. 8E, the silicon nitride film 402, themetal compound film 404 and the gate electrode film 406 are etched toform a predetermined shape, thereby obtaining a gate electrode.Thereafter, side walls 410 are formed onto side faces of the gateelectrode and an impurity is introduced into the gate electrode and thesurface of the silicon substrate 400 in both sides thereof. As describedabove, the MOSFET shown in FIG. 8F is manufactured.

Since the gate insulating film in the MOSFET according to the presentembodiment includes the metal compound film 404 (thin film), which isformed by employing the process for forming the metal compound filmdescribed in the first embodiment or the second embodiment, thepenetration of an impurity contained in the gate electrode film 406through the gate insulating film into the silicon substrate 400 can beeffectively prevented. Having such configuration, the transistors havinghigher reliability can be obtained.

Fifth Embodiment

The present embodiment relates to a cylinder type metal-insulator-metal(MIM) capacitor device. FIG. 9 is a view showing a schematic structureof a capacitor device according to the present embodiment. A cylindertype MIM capacitor device is provided on a transistor having a gateelectrode 323 and a source drain region 324 through a capacitor contact331.

The capacitor device has a multilayered structure comprising a lowerelectrode (first electrode) 340, a capacitor film 342, an upperelectrode 344 and a tungsten film 346, which are formed in this orderand are patterned to a predetermined shape. Further, a bit line 329 isformed on the transistor through a cell contact 328.

Although the bit line 329 and the capacitor contact 331 are illustratedin the same cross-sectional view in FIG. 9, the illustration is made forhelping to understand the whole structure thereof, and in reality, thesedo not intersect. More specifically, the bit line 329 is disposed withina gap in a region where the capacitor contact 331 is provided.

The available deposition source materials for depositing the capacitorfilm 342 may include Zr(N(C₂H₅)₂)₄, Zr(N(CH₃)₂)₄, Zr(N(CH₃)(C₂H₅))₄,Hf(N(C₂H₅)₂)₄, Hf(N(CH₃)₂)₄, Hf(N(CH₃)(C₂H₅))₄ and the like. Even ifsuch chemical compounds are selected, the unreacted organic compound 180of such chemical compounds can be immobilized by conducting theabove-described processing method after the deposition process to cleanthe interior of the vapor phase deposition apparatus 100. Thus,contamination of the particles in the film is inhibited even thoughanother wafer then is loaded in the interior of the vapor phasedeposition apparatus 100 and the deposition is further conducted. As aresult, the capacitor film providing lower leakage current and havingbetter film quality can be obtained.

Typical oxidizing gas employed for depositing the capacitor film 342includes oxygen or a chemical compound containing oxygen. Morespecifically, the typical compounds may be NO, NO₂, N₂O, H₂O, O₂, O₃ andthe like. Among these compounds, NO, NO₂ and N₂O are preferable, and agaseous mixture of NO and NO₂ and a gaseous mixture of NO and O₃, whichrepresent combinations of nitriding gas and oxidizing gas, are morepreferable. The capacitor film having better film quality can be stablydeposited by selecting such combination of gases.

In the deposition process for the capacitor film 342 employing theabove-described source materials, the method for depositing the metalcompound film described in the first embodiment or the second embodimentis employed.

Since the capacitor film 342 contains the metal compound film that isformed by using the method for depositing the metal compound filmdescribed in the first embodiment or the second embodiment in thecylinder type MIM device element according to the present embodiment,contamination of the particles in the capacitor film 342 can beeffectively inhibited. Therefore, the cylinder type MIM capacitor devicehaving higher reliability can be obtained.

While the embodiments of the present invention have been described abovein reference to the annexed figures, it should be understood that thediscriptions above are presented for the purpose of illustrating thepresent invention, and various configurations other than theabove-described configurations can also be adopted.

For example, an oxidizing gas containing Zr(NRR′)₄ or Hf(NRR′)₄ isemployed for the source gas in the above-described embodiment to depositfilms containing compounds such as ZrO₂ or HfO₂ using an ALD techniqueor a CVD technique. In this occasion, in the interior of the chamber1060 of the vapor phase deposition apparatus 100, the wafer having thethin film formed thereon is unloaded from the interior of the vaporphase deposition apparatus 100, and the oxidizing gas is introduced inthe interior of the chamber 1060 to immobilize the unreacted organiccompound 180 during the time when deposition process is not conducted.

In addition, a purge process is typically conducted in the interior ofthe chamber 1060, when the deposition process is not conducted therein.The unreacted organic compound 180 is immobilized by flowing theoxidizing gas in the purge process. In the case of conducting the purgeprocess by using the inert gas and the oxidizing gas, the purge processmay be separated into a purge process by using only the inert gas and apurge process by using only the oxidizing gas.

In addition, while the method for supplying the source material such asTEMAZ into the chamber 1060 in the above-described embodiment employs adownflow system, in which the shower head 108 is provided on the upperportion of the chamber 1060, another configuration, in which the showerhead 108 is provided on a side of the chamber 1060, may alternatively beemployed. By employing the method for depositing the metal compound filmaccording to the present invention, even if such another configurationis employed, the immobilization of the unreacted organic compound 180derived from the source gas such as TEMAZ is inhibited. Therefore, thehigh dielectric constant film having higher quality can be stablyobtained.

It is apparent that the present invention is not limited to the aboveembodiment, that may be modified and changed without departing from thescope and spirit of the invention.

1. A method for processing an interior of a vapor phase depositionapparatus, after conducting a deposition of a thin film by utilizing anorganic source material within said vapor phase deposition apparatus,comprising: immobilizing an unreacted organic compound within theinterior of said vapor phase deposition apparatus, said unreactedorganic compound being derived from said organic source materialremained in the interior of said vapor phase deposition apparatus byintroducing a reactive gas into the interior of said vapor phasedeposition apparatus.
 2. The method according to claim 1, furthercomprising: removing an immobilized material from the interior of saidvapor phase deposition apparatus after said immobilizing the unreactedorganic compound, said immobilized material being formed by immobilizingsaid unreacted organic compound.
 3. The method according to claim 1,wherein said immobilizing the unreacted organic compound includesintroducing an oxidizing gas as said reactive gas.
 4. The methodaccording to claim 3, wherein said immobilizing the unreacted organiccompound further includes additionally introducing a nitriding gas assaid reactive gas.
 5. The method according to claim 3, wherein saidintroducing the oxidizing gas includes introducing O₃ gas as saidoxidizing gas.
 6. The method according to claim 1, wherein said organicsource material contains one or more element(s) selected from a groupconsisting of Hf, Zr, La, Pr, Pb, Sr, Ti and Bi.
 7. A method for forminga thin film by employing a vapor phase deposition apparatus, comprising:processing an interior of a vapor phase deposition apparatus byemploying said method for processing the interior of said vapor phasedeposition apparatus according to claim 1; and forming a thin filmwithin the interior of said vapor phase deposition apparatus afterprocessing the interior of said vapor phase deposition apparatus.
 8. Themethod according to claim 7, wherein said forming the thin filmincluding forming the thin film by employing an organic source materialthat contains one or more element (s) selected from a group consistingof Hf, Zr, La, Pr, Pb, Sr, Ti and Bi.
 9. A method for manufacturing asemiconductor device by employing a vapor phase deposition apparatus,comprising: forming a thin film on a semiconductor substrate within aninterior of said vapor phase deposition apparatus; unloading saidsemiconductor substrate having said thin film formed on saidsemiconductor substrate from the interior of said vapor phase depositionapparatus after forming said thin film on said semiconductor substrate;processing the interior of said vapor phase deposition apparatus byemploying said method for processing said vapor phase depositionapparatus according to claim 1, after unloading said semiconductorsubstrate; and forming a thin film on another semiconductor substrate,after processing the interior of said vapor phase deposition apparatusand loading said another semiconductor substrate in the interior of saidvapor phase deposition apparatus.
 10. The method according to claim 9,wherein said processing the interior of said vapor phase depositionapparatus is carried out in every time after a plurality ofimplementations of said forming the thin film on said semiconductorsubstrate and said forming the thin film on said another semiconductorsubstrate are conducted.
 11. The method according to claim 9, whereinsaid processing the interior of said vapor phase deposition apparatus iscarried out in every time after forming said thin film on a plurality ofsemiconductor substrate.
 12. The method according to claim 9, furthercomprising removing said immobilized material from the interior of saidvapor phase deposition apparatus, said immobilized material being formedby immobilizing said unreacted organic compound.
 13. The methodaccording to claim 12, wherein said removing said immobilized materialis carried out after a plurality of implementations of said immobilizingsaid unreacted organic compound are carried out.
 14. The methodaccording to claim 9, wherein said forming the thin film on saidsemiconductor substrate and forming the thin film on said anothersemiconductor substrate including forming the thin film by employing anorganic source material that contains one or more element(s) selectedfrom a group consisting of Hf, Zr, La, Pr, Pb, Sr, Ti and Bi.